Niobium silicate as a filler for an experimental photopolymerizable luting agent.

PURPOSE: To synthesize niobium silicate particles (SiNb) and incorporate into resin-based luting agents. METHODS: SiNb particles were synthesized and characterized by x-ray diffraction, FTIR spectroscopy, particle size, and specific surface area. Luting agents were formulated with 50 wt% BisGMA, 30 wt% TEGDMA and 20 wt% UDMA. BAPO was used as a photoinitiator in 1mol%. The SiNb particles were incorporated into the agents at concentrations of 50 wt% (SiNb50%) or 65% wt% (SiNb65%). Barium glass particles at the same concentrations were used as controls (SiBa50% and SiBa65%). Refractive index, degree of conversion (DC), polymerization kinetics, softening in solvent, radiopacity, film thickness, color stability, flexural strength (FS) and micro shear bond strength (µSBS) were evaluated. RESULTS: SiNb particles were successfully synthesized with an adequate structure to be applied as inorganic fillers. SiNb groups had higher DC, lower %ΔKHN, greater film thickness and greater radiopacity than the SiBa groups. Color stability was greater for SiNb50% and SiNb65% after six months of storage, as demonstrated by ΔE00. ΔWID values were lower for the SiBa groups. FS results decreased over time, and lower values were found for SiNb. In µSBS, the values of SiNb65% were higher at 24 h (45.22 MPa) and at six months (36.83 MPa), with statistically differences from values for the SiBa groups. CONCLUSIONS: SiNb particles were successfully synthesized using the sol-gel method, and their incorporation into luting agents at a concentration of up to 65% improved the physicomechanical characteristics and color stability of these agents.

Myristyltrimethylammonium Bromide (MYTAB) as a Cationic Surface Agent to Inhibit Streptococcus mutans Grown over Dental Resins: An In Vitro Study.

This in vitro study evaluated the effect of myristyltrimethylammonium bromide (MYTAB) on the physical, chemical, and biological properties of an experimental dental resin. The resin was formulated with dental dimetacrylate monomers and a photoinitiator/co-initiator system. MYTAB was added at 0.5 (G0.5%), 1 (G1%), and 2 (G2%) wt %, and one group remained without MYTAB and was used as the control (GCtrl). The resins were analyzed for the polymerization kinetics, degree of conversion, ultimate tensile strength (UTS), antibacterial activity against Streptococcus mutans, and cytotoxicity against human keratinocytes. Changes in the polymerization kinetics profiling were observed, and the degree of conversion ranged from 57.36% (±2.50%) for G2% to 61.88% (±1.91%) for G0.5%, without a statistically significant difference among groups (p > 0.05). The UTS values ranged from 32.85 (±6.08) MPa for G0.5% to 35.12 (±5.74) MPa for GCtrl (p > 0.05). MYTAB groups showed antibacterial activity against biofilm formation from 0.5 wt % (p < 0.05) and against planktonic bacteria from 1 wt % (p < 0.05). The higher the MYTAB concentration, the higher the cytotoxic effect, without differences between GCtrl e G0.5% (p > 0.05). In conclusion, the addition of 0.5 wt % of MYTAB did not alter the physical and chemical properties of the dental resin and provided antibacterial activity without cytotoxic effect.

Ionic liquid as antibacterial agent for an experimental orthodontic adhesive.

OBJECTIVE: The aim of this study was to formulate and evaluate experimental orthodontic adhesives with different concentrations of 1-n-butyl-3-methylimidazoilium bis(trifluoromethanesulfonyl)imide (BMIM.NTf2). METHODS: The experimental orthodontic adhesives were formulated with methacrylate monomers, photoinitiators and silica colloidal. The ionic liquid BMIM.NTf2 was synthesized and characterized. BMIM.NTf2 was added at 5 (G5%), 10 (G10%) and 15 (G15%) wt.%. One group contained no BMIM.NTf2 to function as control (GCtrl). The adhesives were evaluated for polymerization kinetics, degree of conversion (DC), Knoop hardness and softening in solvent, ultimate tensile strength (UTS), shear bond strength (SBS), thermogravimetric analysis (TGA), antibacterial activity and cytotoxicity. RESULTS: BMI.NTf2 showed the characteristic chemical peaks. The polymerization kinetics were different among the groups. G10% and G15% showed higher DC (p < 0.05). G5% and GCtrl had no differences for softening in solvent (p > 0.05). There were no differences for UTS (p > 0.05) and SBS (p > 0.05). TGA showed one different peak for G15%. All groups with BMIM.NTf2 showed antibacterial activity compared to GCtrl (p < 0.05) without cytotoxicity (p > 0.05). SIGNIFICANCE: To reduce biofilm formation around brackets and to prevent demineralization at susceptible sites, materials have been developed with antibacterial properties. In this study, a new experimental orthodontic adhesive was formulated with an imidazolium ionic liquid (BMIM.NTf2) as antibacterial agent. The incorporation of 5 wt.% of ionic liquid decreased biofilm formation without affecting the physico-chemical properties and cytotoxicity of an experimental orthodontic resin.

Polímero de MMA para base de dentadura com a adição de subnitrato de bismuto / Addition of bismuth subnitrate in denture base MMA polymer

Objetivo: o presente estudo tem por objetivo avaliar a influência da adição de diferentes concentrações de subnitrato de bismuto (SN) nas propriedades de mate-riais para base protética. Materias e método: foi adicio-nada 0%, 1%, 2%, 5%, 10% e 20% de SN em peso em resina acrílica autopolimerizável da marca Clássico e submetidos aos ensaios de resistência à flexão, micro-dureza Knoop, radiopacidade, análise antimicrobiana, rugosidade e caracterização em micro-Raman. O teste estatístico escolhido foram o ANOVA de uma via e o teste de comparações múltiplas de Tukey. O nível de significância foi de 5% para todos os testes. Resultados: os resultados de resistência à flexão atingiram valores acima do recomendado pela ISO 1567. Quanto maior a concentração da carga de SN maior o valor de mi-crodureza Knoop, sendo estatisticamente significativo em 10% e 20% (p<0,001); os resultados da rugosidade mostraram valores abaixo do limiar, 0,2 µm. A adição de subnitrato de bismuto não obteve um potencial an-timicrobiano, mas apresentou uma maior radiopacida-de, (p<0,001). Conclusão: diante dos dados, conclui-se que a adição da carga de SN influencia nas proprie-dades mecânicas de resina acrílica significativamente, destacando-se que a radiopacidade desse material faci-lita a sua remoção quando ingerida ou aspirada.